Synthesis of high surface area CaSO4 center dot 0.5H(2)O nanorods using calcium ethoxide as precursor
Metadatos
Mostrar el registro completo del ítemAutor
Burgos Ruiz, Miguel; Pelayo Punzano, Gloria; Ruiz Agudo, Encarnación; Elert, Kerstin; Rodríguez Navarro, Carlos ManuelEditorial
Royal Society of Chemistry
Fecha
2021-07-05Referencia bibliográfica
Chem. Commun., 2021, Advance Article. DOI: [10.1039/d1cc02014e]
Patrocinador
Spanish Government European Commission PRE2019-090256 RTI2018-099565-B-I00; Junta de Andalucia RNM-179; University of Granada, UGR UCE-PP2016-05Resumen
We report a novel solvothermal route for the production of bassanite (CaSO4 center dot 0.5H(2)O) nanoparticles using amorphous Ca-ethoxide as a precursor. Bassanite nanorods, 120-200 nm in length, with the highest specific surface area reported so far (54 m(2) g(-1)) and enhanced reactivity, are obtained at 78 degrees C and 1 atm. Such nanoparticles may find application in several fields, including biomaterials, drug delivery, and cultural heritage conservation.