Title: A novel bioactive agent improves adhesion of resin-modified glass-ionomer to dentin
Authors: Osorio Ruiz, Estrella
Ticiane, Fagundes
Navarro, Maria Fidela
Zanotto, Edgar D.
Peiti, Oscar
Osorio Ruiz, Raquel
Toledano-Osorio, Manuel
Toledano Pérez, Manuel
Issue Date: 2015
Abstract: Bioactive glasses are surface-active materials able induce remineralization of dental structure. Objectives: to evaluate the effect of doping two resin-modified glass ionomer cements (RMGICs) with a bioactive glass (Biosilicate) in compressive and microtensile bond strength (MTBS) to dentin. Methods: Experimental powders were made by incorporating 2, 5, and 10 wt% of biosilicate in Vitremer (VT) and Fuji II LC (FL) powder. FL and VT were used as control materials. Six cylinders of each experimental material were tested for failure in compression at 1.0mm/min, after 24h storage in distilled water at 37ºC. For the bond strength test, thirty non-carious human molars underwent cavity preparation previous to restoration. Restorative materials were VT or FL with and without 2 wt% biosilicate. The teeth were stored in water at 37ºC for 24h or 7d, sectioned into beams, and tested for failure in tension at 0.5 mm/min. Compressive and bond strength data were analyzed by analysis of variance and multiple-comparison tests (p<0.05). Analysis of de-bonded specimens was performed by scanning electron microscopy (SEM). Results: Only incorporation of 2 wt% of biosilicate did not decrease the compressive strength of the tested RMGICs. The incorporation of 2 wt% biosilicate into RMGICs produced and increase in bond strength after 24h for FL, and after 24h and 7d for VT. Significance: Incorporation of 2 wt% of biosilicate particles into RMGICs did not affect the compressive strength and improved bond strength to dentin.  
Sponsorship: CICOM/FEDER MAT 2011-24551; JA-P08-CTS-3944 and Fapesp 07/08179-7.
Publisher: Taylor & Francis
Description: “This is an Accepted Manuscript of an article published by Taylor & Francis in Journal of Adhesion Science and Technology on 2015-05-05, available online: http://www.tandfonline.com/10.1080/01694243.2015.1030897.”
Keywords: Resin-modified glass-ionomer cement
Bioactive materials
URI: http://hdl.handle.net/10481/41608
ISSN: 0169-4243
Rights : Creative Commons Attribution-NonCommercial-NoDerivs 3.0 License
Citation: Osorio, E.; et al. A novel bioactive agent improves adhesion of resin-modified glass-ionomer to dentin. Journal Adhesion Science and Technology, 29(15): 1543–1552 (2015). [http://hdl.handle.net/10481/41608]
Appears in Collections:CTS242 - Artículos

Files in This Item:

File Description SizeFormat
Osorio_BioactiveMaterials.pdf595.11 kBAdobe PDFView/Open
Recommend this item

This item is licensed under a Creative Commons License
Creative Commons

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.


Valid XHTML 1.0! OpenAire compliant DSpace Software Copyright © 2002-2007 MIT and Hewlett-Packard - Feedback

© Universidad de Granada