Silver improves collagen structure and stability at demineralized dentin: a dynamic-mechanical and Raman analysis.
Metadatos
Mostrar el registro completo del ítemAutor
Osorio Ruiz, María Estrella; Toledano Osorio, Manuel; Osorio Ruiz, Raquel; Sánchez Aguilera, Fátima; Medina Castillo, Antonio Luis; Toledano Pérez, Manuel; Toledano Osorio, ManuelMateria
Collagen Erosion Demineralisation Dentine Microscopy Raman
Fecha
2018-10Referencia bibliográfica
Osorio R, Osorio E, Aguilera FS, Medina-Castillo AL, Toledano M, Toledano-Osorio M. Silver improves collagen structure and stability at demineralized dentin: A dynamic-mechanical and Raman analysis. J Dent. 2018 Oct 5. pii: S0300-5712(18)30537-2. [http://hdl.handle.net/10481/53637]
Patrocinador
This work was supported by the Ministry of Economy and Competitiveness (MINECO) and European Regional Development Fund (FEDER). Project MAT2017-85999-P MINECO/AEI/FEDER/UE.Resumen
Objective: This study aimed to evaluate the effect of silver loaded nanoparticles (NPs) application on dentin remineralization.
Methods: Polymethylmetacrylate-based NPs and silver loaded NPs (Ag-NPs) were applied on demineralized dentin surfaces. Dentin was characterized morphologically by scanning electron microscopy, mechanically probed by a nanoindenter to test nanohardness and Young modulus, and chemically analyzed by Raman spectroscopy after 24 h and 7 d of storage. Untreated surfaces were used as control. Data were submitted to ANOVA and Student-Newman-Keuls multiple comparisons tests (P<0.05).
Results: After Raman analysis, dentin treated with Ag-NPs obtained the lowest mineralization and intensity of stoichiometric hydroxyapatite when compared with specimens treated with undoped-NPs. The lowest relative mineral concentration, expressed as the ratio phosphate or carbonate/phenyl group, and crystallinity was attained by dentin treated with with Ag-NPs, after 7 d. Ag-NPs application generated the highest values of collagen crosslinking (intensity at 1032 cm-1 band). The molecular conformation of the collagen’s polypeptide chains, amide-I and CH2 also attained the highest peaks in dentin treated with Ag-NPs. Staggered and demineralized collagen fibrils were observed covering the dentin surfaces treated with Ag-NPs, at both 24 h and 7 d. Samples treated with Ag-NPs attained the lowest values of nanohardness and Young’s modulus at 7 d of storage.
Conclusions: Peritubular and intertubular dentin were remineralized when using undoped-NPs. After 7 d, collagen treated with NPs was remineralized but dentin treated with Ag-NPs attained an improved collagen matrix structure and stability but the lowest mineralization and crystallinity.