Submicron-to-nanoscale structure characterization and organization of crystals in dentin bioapatites Toledano Pérez, Manuel Sánchez Aguilera, Fátima Osorio Ruiz, María Estrella López López, Modesto Torcuato Cabello Malagón, Inmaculada Toledano Osorio, Manuel Osorio Ruiz, Raquel Dentin Cristallinity X-ray diffraction Transmission Electron Microscopy Hydroxyl-apatite The aim of this research was to ascertain the crystal morphology, and to assess the ultrastructure and texture changes of sound (SD) and caries-affected dentin (CAD) after being restored with Zn-free and Zn-containing amalgam. Dentin surfaces were studied by X-ray diffraction (XRD2), and Transmission Electron Microscopy (TEM) through selected area diffraction (SAED) and bright-field (BF) imaging. Crystals, at the dentin surface, were identified as hydroxyl-apatite with augmented crystallographic maturity, crystallite and grain sizes, and lower microstrain, in CAD dentin after Zn-containing amalgam removal, at 310 plane. This group, at this reflection, achieved lower microstrain than before amalgam placement. Opposed trend was followed at 002 reflection. Texture increased in CAD at both reflections, after the removal of Zn-containing amalgams. Crystallinity increased in SD after amalgam restorations at 002 and 310 reflections. In CAD, crystallinity decreased after amalgam restorations at 002 plane. Block-like and needle-like apatite crystals constituted the bulk of minerals in SD. Needle-like apatite crystals were observed, in CAD surfaces, before and after Zn-free amalgam restorations. Polyhedral and rounded drop-like shaped crystals characterized the CAD surfaces before Zn-containing amalgam placement. After the restoration removal, plate-like polygons and three-dimensional agglomerated crystals were determined. Crystallites, with improved crystallographic orientation, became shorter and thinner in CAD treated with Zn-containing amalgams, thus increasing mineralization and maturity. 2016-06-08T07:19:40Z 2016-06-08T07:19:40Z 2016-05 info:eu-repo/semantics/article Toledano Pérez, M.; et al. Submicron-to-nanoscale structure characterization and organization of crystals in dentin bioapatites. RSC Advances, 6: 45265–45278 (2016). [http://hdl.handle.net/10481/41632] 2046-2069 http://hdl.handle.net/10481/41632 10.1039/C6RA02373H eng http://creativecommons.org/licenses/by-nc-nd/3.0/ info:eu-repo/semantics/openAccess Creative Commons Attribution-NonCommercial-NoDerivs 3.0 License Royal Society of Chemistry