Effect of aging process on mechanical performance of reinforced mortar with NaOH abaca fibers
Metadatos
Mostrar el registro completo del ítemAutor
Alcivar-Bastidas, S.; Petroche, Daniel M; Cornejo, Mauricio H.; Martínez-Echevarría Romero, María JoséEditorial
Elsevier
Materia
Abaca fibers Alkaline treatment Mechanical properties
Fecha
2024-04-02Referencia bibliográfica
Alcivar-Bastidas, Stefany, et al. Effect of aging process on mechanical performance of reinforced mortar with NaOH abaca fibers. Case Studies in Construction Materials 20 (2024) e03122 [10.1016/j.cscm.2024.e03122]
Patrocinador
Universidad Católica de Santiago de Guayaquil under Grant Cod. Pre 515, cod Int. 326Resumen
There is a high demand for bio composites due to its eco-friendliness, lightweight, availability,
low cost and life-cycle superior. This bio composite was prepared by reinforcing the cementitious
matrix with alkali treated abaca fiber. However, one of the major concerns about this material is
its durability in the cementitious matrix. This study gives an insight into the comparison of alkali
treated fiber reinforced mortar (MFTHS) vs reference mortar with no fiber (MSF) through flexural,
compressive, shrinkage and tensile test at 28 days, it also compared two processes of wet/dry cycles subjecting samples to the same mechanical properties. MFTHS increased its mechanical
properties for an average of 25% compared to MSF. The same pattern occurs after applying WD-1
and WD-2, MFTHS showed better bonding between the matrix and the treated abaca fiber.