@misc{10481/41608,
year = {2015},
url = {http://hdl.handle.net/10481/41608},
abstract = {Bioactive glasses are surface-active materials able induce remineralization of dental structure. Objectives: to evaluate the effect of doping two resin-modified glass ionomer cements (RMGICs) with a bioactive glass (Biosilicate) in compressive and microtensile bond strength (MTBS) to dentin. Methods: Experimental powders were made by incorporating 2, 5, and 10 wt% of biosilicate in Vitremer (VT) and Fuji II LC (FL) powder. FL and VT were used as control materials. Six cylinders of each experimental material were tested for failure in compression at 1.0mm/min, after 24h storage in distilled water at 37ºC. For the bond strength test, thirty non-carious human molars underwent cavity preparation previous to restoration. Restorative materials were VT or FL with and without 2 wt% biosilicate. The teeth were stored in water at 37ºC for 24h or 7d, sectioned into beams, and tested for failure in tension at 0.5 mm/min. Compressive and bond strength data were analyzed by analysis of variance and multiple-comparison tests (p<0.05). Analysis of de-bonded specimens was performed by scanning electron microscopy (SEM). Results: Only incorporation of 2 wt% of biosilicate did not decrease the compressive strength of the tested RMGICs. The incorporation of 2 wt% biosilicate into RMGICs produced and increase in bond strength after 24h for FL, and after 24h and 7d for VT. Significance: Incorporation of 2 wt% of biosilicate particles into RMGICs did not affect the compressive strength and improved bond strength to dentin.
 },
organization = {CICOM/FEDER MAT 2011-24551; JA-P08-CTS-3944 and Fapesp 07/08179-7.},
publisher = {Taylor & Francis},
keywords = {Resin-modified glass-ionomer cement},
keywords = {Dentin},
keywords = {Adhesion},
keywords = {Compression},
keywords = {Bioactive materials},
title = {A novel bioactive agent improves adhesion of resin-modified glass-ionomer to dentin},
doi = {10.1080/01694243.2015.1030897},
author = {Osorio Ruiz, María Estrella and Ticiane, Fagundes and Navarro, Maria Fidela and Zanotto, Edgar D. and Peiti, Oscar and Osorio Ruiz, Raquel and Toledano Osorio, Manuel and Toledano Pérez, Manuel},
}