Aplicabilidad de las margas de la Cordillera Bética (sur de la provincia de Jaén) para la fabricación de baldosas cerámicas prensadas Vázquez Vílchez, María Mercedes Jiménez-Millán, Juan Formación Carbonero Baldosas prensadas Materia prima cerámica Materiales de construcción Propiedades tecnológicas Carbonero formation Pressed tiles Ceramic prime material Construction materials Technological properties Este trabajo evalúa las posibilidades cerámicas de las margas de la Formación Carbonero para fabricar materiales cerámicos de construcción de alto valor añadido. Litológicamente, la Formación Carbonero está formada por tres miembros: a) Inferior Margoso, b) Intermedio Radiolarítico y c) Superior Turbidítico. Las muestras estudiadas son ricas en filosilicatos (> 39%) y calcita. Los contenidos en cuarzo y feldespatos son bajos (< 27%). Los filosilicatos mayoritarios son el interestratificado illita-esmectita (14-50%) y la illita (32-74%). Caolinita, clorita y paligorskita están en pequeñas cantidades. Los mayores contenidos en CaO están en las margas de los Miembros Inferior e Intermedio (18-27%). Las margas molidas presentan similares proporciones granulométricas de las fracciones < 2 μm y de la situada entre 2 y 20 μm. La fracción > 20 μm está ausente. La plasticidad de las margas es baja, condicionando que su moldeo deba ser exclusivamente por presión. Los altos valores de contracción lineal y absorción de agua entre 800 y 1.000 ºC son poco apropiados para la industria cerámica. Las mezclas de estos materiales con diferentes proporciones de materiales complementarios permitirían la fabricación de baldosas cerámicas de color claro por prensado. This paper assesses the aptness of Carbonero Formation (in the Spanish province of Jaén) marls for the manufacture of high added value ceramic construction materials. Lithologically speaking, the Carbonero Formation comprises three members: a) a marly lower member; b) a radiolaritic middle member; and c) a turbiditic upper member. The samples studied were rich in phyllosilicates (> 39%) and calcite. The quartz and feldspar contents were low (< 27%). The majority phyllosilicates were illite-smectite mixed layers (14-50%) and illite (32-74%). Kaolinite, chlorite and palygorskite were also detected. The highest CaO content was found in the marls in the lower and intermediate members (18-27%). The particle size distributions of ground marls were similar for the < 2 μm and 2-20 μm fractions. The > 20 μm fraction was absent. Due to their low plasticity, most Carbonero Formation marls can only be pressure moulded. Their high linear shrinkage and water absorption values when fired at 800 to 1,000 ºC make them poorly suited for use in the ceramic industry. Blends of these marls with different proportions of supplementary materials may be apt for manufacturing light shades of pressed ceramic tile. 2014-09-19T10:47:21Z 2014-09-19T10:47:21Z 2009 info:eu-repo/semantics/article Vázquez, M.; Jiménez-Millán, J. Aplicabilidad de las margas de la Cordillera Bética (sur de la provincia de Jaén) para la fabricación de baldosas cerámicas prensadas. Materiales de Construcción, 59(294): 97-112 (2009). [http://hdl.handle.net/10481/33095] 0465-2746 1988-3226 http://hdl.handle.net/10481/33095 10.3989/mc.2009.40707 eng spa http://creativecommons.org/licenses/by-nc-nd/3.0/ info:eu-repo/semantics/openAccess Creative Commons Attribution-NonCommercial-NoDerivs 3.0 License Consejo Superior de Investigaciones Científicas (CSIC)